Nickel-based alloy is a special type of alloy that mainly contains nickel, while doping a small amount of other elements, such as iron, chromium, manganese and so on. This alloy has excellent corrosion resistance and high temperature strength. Nickel-based alloy powder is a fine powder material composed of tiny nickel-based alloy particles. Compared with traditional metal powders, nickel-based alloy powders have higher corrosion resistance and high temperature properties. During the manufacturing process, these particles are finely melted and ground to ensure their excellent physical and chemical properties. Nickel-based alloy powder has a wide range of uses and can be used to manufacture high-performance components and structural materials.
Item | Technology | Flow | Density | Hardness | Size | Content | Applications |
HRNi20A | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 18-22HRC | -106+45um -90+45um |
C:0.1 Cr:4.5 Si:2.0 B:0.7 Ni:bal. |
Flame spray/fusing,Glass mould, various casting dies. |
HRNi22A | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 20-24HRC | -106+45um -90+45um |
C:0.2 Cr:1.0 Si:2.8 B:1.4 Fe:1.0 Mn:0.1 Ni:bal. |
Flame spray/fusing Glass mould, various casting dies. |
HRNi25 | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 22-27HRC | -106+45um -90+45um |
C:0.2 Cr:1.0 Si:3.5 B:1.5 Fe:8.0 Ni:bal. |
Flame spray/fusing Glass mould, various casting dies. |
HRNi28A | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 26-30HRC | -106+45um -90+45um |
C:0.1 Cr:3.0 Si:2.6 B:1.0 Ni:bal. |
Flame spray/fusing Glass mould, various casting dies. |
HRNi35 | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 32-37HRC | -106+45um -90+45um |
C:0.3 Cr:10 Si:3.5 Fe:10 B:2.0 Ni:bal. |
Flame spray/fusing Glass mould, various casting dies. |
HRNi37A | Gas Atomized | 12-17s/50g | 3.5-4.5g/cm3 | 35-40HRC | -106+45um -90+45um |
C:0.15 Cr:4.5 Si:2.6 B:1.2 Ni:bal. |
Flame spray/fusing Glass mould, various casting dies. |
HRNi45A | Water atomized | 17-21s/50g | 3.5-4.5g/cm3 | 42-47HRC | -106+45um -90+45um |
C:0.4 Si:3 B:2.6 Cr:12 Fe:5 Ni:bal. |
Flame spray/fusing HVOF, Seal surface, punch,valve, piston etc. |
HRNi50A | Water atomized | 17-21s/50g | 3.5-4.5g/cm3 | 45-50HRC | -106+45um -90+45um |
C:0.5 Si:3.0 B:3.0 Cr:12 Fe:5 Ni:bal. |
Flame spray/fusing HVOF, Seal surface, oil plunger and shaft etc. |
HRNi55A | Water atomized | 17-21s/50g | 3.5-4.5g/cm3 | 52-55HRC | -106+45um -90+45um |
C:0.8 Si:4.0 B:3.0 Cr:14 Fe:5.0 Ni:bal. |
Flame spray/fusingHVOF, Seal surface, oil plunger and shaft etc. |
HRNi60A | Water atomized Gas atomized | 17-21s/50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um |
C:0.9 Si:4.0 B:3.2 Cr:16 Fe:5.0 Ni:bal. |
Flame spray/fusing HVOF, good corrosion resist, high hardness, good wear resist performance, low friction coefficient. |
HRNi60CuMo | Water atomized Gas atomized |
17-21s/50g | 3.5-4.5g/cm3 | 55-60HRC | -106+45um -90+45um |
C:0.9 Si:4.0 B:4.0 Cr:16 Cu:3.0 Mo:3.0 Fe:5.0 Ni:bal. |
Flame spray/fusing HVOF,fix, impeller, piston, valve etc. |
HRNi65A | Water atomized | 17-21s/50g | 3.5-4.5g/cm3 | 60-65HRC | -106+45um -90+45um |
C:1.1 Si:4.0 B:4.0 Cr:18 Fe:5.0 Ni:bal. |
Flame spray/fusingHVOF, higher hardness than Ni60A, wire roller, plunger, conveyor roller etc. |
HRNI625 | Water atomized Gas atomized | 17-21s/50g | 3.5-4.5g/cm3 | 8-15HRC | -106+45um -90+45um -45+15um |
C:0.1 Si:0.5 B:0.5 Cr:21 Mo:8.5 Nb:4.0 Fe:5.0 Mn:0.5 Ni:bal. |
Flame spray/fusing HVOF, good corrosion resst and anti-high temperature oxided performance, |
PS: We also offer customized services |
1.Covering special layer on iron and steel parts and some glass moulds repairing.
2.Pre-protection and repairing or strengthening merchannical parts.
3.For FLS/PTA/APS/Laser Cladding application with blending Ni or Nickel base alloy powder layers.
4.Generate more dense coating compared with FTC, and with better hardness and wearness.